Content：
r.tecc Norplex MLK 2
Lithium Complex EP Grease – NLGI-Grade 2
|
Description |
r.tecc Norplex MLK 2 / Rhenus Norplex MLK 2 is a high performance EP-grease based on high quality synthetic oil. |
|
Application
and
Properties |
r.tecc Norplex MLK 2 / Rhenus Norplex MLK 2 is designed for lubrication of high pressure and impact loaded anti-friction and roller bearings in a wide range of useful temperatures.
r.tecc Norplex MLK 2 / Rhenus Norplex MLK 2 is a low temperature grease on synthetic oil basis covering also the range of application of a high temperature grease.
r.tecc Norplex MLK 2 / Rhenus Norplex MLK 2 is specially designed for the lubrication of high-speed spindle bearings.
Advantages:
low starting resistance at low temperatures
high thermal load capacity
worked stability
oxidation stability
high pressure load capacity
good water resistance
good corrosion protection |
|
Technical Data
|
| Thickener |
|
Lithium-Complex-Soap |
| Operating temperature for long-term lubrication |
|
-50 to +150℃ |
| Short time admissible temperature peak value |
|
+200℃ |
| Permanent temperatures above 150℃ require re-greasing at shorter intervals subject to thermal load |
| Drop point |
ASTM D 2265 |
> 270℃ |
| Worked penetration after 60 strokes |
ASTM D 217 |
265 to 295 1/10 mm |
| Type of base oil |
|
Synthetic |
| Base oil viscosity at 40℃ |
ASTM D 445 |
30 mm²/s |
| Water resistance |
DIN 51 807 T1 |
1 – 90 |
| SKF Emcor Test |
IP 220/85 |
Corrosion degree 0/0 |
| Copper Strip Test |
ASTM D 4048 |
Corrosion degree 1 - 150 |
| FAG-FE9 - Test |
DIN 51821-02-A/
1500/6000-150 |
F50 > 120 h |
| FAG-FE8 - Test, 536050TVP angular ball bearing |
E DIN 51 819-02-6000/5-RT |
mw = 19 / 20 mg |
FAG-R6 - Test
Friction Moment Measurement Fa = 179 N, Fr = 23 N, 7500 min-1 |
FAG - Method |
MH1 = 9 Ncm
MB = 1 Ncm
Grease loss ≌ 9 mg
LB ≌ 10 h |
| FAG-WS22 Spindle bearing Test |
FAG - Method |
F50 > 9000 h |
| Designation |
DIN 51 502 |
KPHC 2 P-50 |
Subject to modification of the technical data. Please refer to the material safety data sheet for additional information or contact our application engineers. |